Advantages
 
Bath Composition and Working Conditions
 
Make up the solution
 
Equipments
 
Functions and addition of the brighteners

● Suitable for barrel nickel plating；
● High-speed brightening with excellent leveling；
● Spotless white and esthetic deposit with good ductility；
● Even nickel layer results from excellent covering power and throwing power；
● Addition of single brightener, so the process is very easy to control；
● Very easy conversion from most bright nickel-plating system by direct addition.
Bath composition & technical data
Application
 Standard
　　　　　NiSO4.6H2O
　　　　　NiCL2.6H2O
　　　　　H3BO3		 　　　　220-280　g/l
　　　　40-60　　g/l
　　　　35-50　　g/l 		　　　250 　g/l
　　　50　　g/l
　　　45　　g/l
　　　　　brightener HN-B
　　　　　　softener HN-5(2X)
　　　　　　assistant HN-1
　　　　　  wetting agent HN-17/HN-19 		 　　　　0.5-1.0　ml/l
　　　　8-12 　　ml/l
　　　　3-5　　　ml/l
　　　　1-1.5　　ml/l 		　　　0.4　ml/l
　　　10　 ml/l
　　　4　　ml/l
　　　1　　ml/l
　　　　　Temperature
　　　　　pH level
　　　　　Voltage		 　　　　50-60。C
　　　　4.0-4.8
　　　　12-16v 		　　　50-60。C
　　　4.5
　　　12-16v

 

●　Fill up a preparatory tank to two-third of the volume with water， and heat it up to 65-70。C；add NiSO4.6H2O and NiCL2.6H2O, and mix them up until they are completely dissolved.
　　Add NiCO3 or 4% NaOH and adjust the PH level to 5.2.  
●　Add 2.5ml/l H2O2(diluted in water) and 2.5ml/l active carbon, and mix them up for several hours. After precipitation for a whole night, filter the solution carefully into the working tank. Now rinse the filter pump and then put in some active carbon. 
●　Add H3BO3 and adjust the PH level to 4.0 with diluted H2SO4 
●　Electrolyze the solution at 0.1-0.5 A/m2 with waved pseufdo-cathode for over 12 hours, or until the deposit in LCD is changed from dark to beige.
●　Finally, add the above additives, and get the solution ready for use. 
 


●　Working tank：　plastic-lined steel tanks or plastic tanks 
●　Circulating filtration： the solution can be filtered at least 4 times within one hour. It can achieve a better effect if the filtration pump is added with  0.6g/l active carbon between each 40 working hours.　　

 

softener HN-5（2X）：　reducing internal stress, increasing softness and improving throwing power at LCD area 
assistant HN-1：　　　　Improving brightness, performing a better leveling. It will also create a more symmetric coat with more brightness in LCD area.
brightener HN-BP：　　　　combined with HN-5(2X) and HN-1, it will get a bright coat within the whole current density range with excellent leveling. Containing certain amount of softener and assistant, it can be complemented with HNBP only in the course of plating; or extra HN-nickel feed water (T. C.)  upon demand.


HN-B consumption： 200-250ml/1000Ah