PRODUCTS
INTRODUCTION
SILANE CROSSLINKABLE
PE CABLE INSULATION COMPOUND
(¢ñ)Application: The product is an ideal
and new material instead of PVC as the insulation
layer of low-voltage power cable.
(¢ò)Technical data:
- High thermal-deformation-resistant capability
and excellent ageing-resistant properties
- The max. Temp. allowed for normal use is 90¡æ
- The max. Temp. allowed for normal use is 130¡æ
- The max. Temp. allowed for emergency use is
250¡æ
(¢ó)Reference values
Typical values for reference are seen in the following
table:
No.
|
Test item
|
Unit
|
SI-70
|
1
|
Density
|
|
0.922 ¡À 0.003
|
2
|
Mechanical properties
|
Tensile strength¡Ý
Elongation at break¡Ý
|
Mpa
%
|
13.50
350
|
3
|
Melt index(E condition)
|
g/10min
|
0.35-1.00
|
4
|
Air drying oven ageing
test
|
|
|
|
|
Ageing conditions
|
Temp.
Time
|
¡æ
hr
|
135¡À3
168
|
|
|
Tensile strength variance
|
%
|
¡À25
|
|
|
Elongation variance
|
%
|
¡À25
|
5
|
Thermal elongation test
|
Temp.
Loading time
|
¡æ
min
|
200¡À3
15
|
|
|
Mechanical stress
Elongation under load¡Ü
Parmanent elongation after
cooling
|
Mpa
%
%
|
0.2
100
10
|
6
|
Electrical properties
|
|
|
|
|
Insulation volume resistance¡Ý
|
¦¸.m
|
1¡Á1014
|
|
|
Dielectric constant¡Ü
|
|
2.30
|
|
|
Dielectric loss angle tangent¡Ü
|
|
¡Á10-4
|
|
|
|
|
|
|
|
Note: All items are tested after SI-70/B-01crosslinking
except for item1,3,7.
(¢ô)Packing
To prevent the product from damp, crosslinkable
PE are packaged with three layers: the outside
layer is brown packing paper, the middle layer
is PE plastic packing bag and the inside layer
is Aluminum foil packing bag. The standard package
is 25kg/bag.
(¢õ)Transportation and storage:
During transportation and handling, it is important
that the product should not be placed in damp
and high-temperature environment or be exposed
to sunshine and rain and the packing bag should
not be destroyed. Because the silane of SI-XLPE
or tube compound can absorb moisture and crosslink,
it is very important to prevent of the product
is half of a year. It is better to use SI-XLPE
or tube compound in opened package as quickly
as possible. If the package has been worn-out
before using SI-XLPE inside it, we suggest that
the SI-XLPE in worn-out package can be used as
common LDPE in order to get quality crosslinked
cable.
|