Unsaturated polyester resin TR-102 gel coat |
| Performance index of Liquid resin: |
|
|
|
| |
|
Unit |
Test standard |
|
| Appearance |
paste-like thixotropic liquid |
|
|
| Acid value |
14-22 |
mgKOH/g |
GB 2895-82 |
| Solid |
65-71 |
% |
GB 7193.3-87 |
| Viscosity at 25℃ |
1.19-2.21 |
Pa.s |
GB 7193.1-87 |
| Thixotropic index |
≥4.5 |
|
|
| Typical curing performance: |
|
|
|
| |
|
Unit |
Test standard |
|
water bath at 25℃, add 2ml methyl ethyl ketone peroxide solution and 4ml Cobalt isooctanoate solution into 100g resin |
| Gel time |
4.9-9.1 |
min |
see GB 7193.6-87 |
| Performance of cured resin: |
|
|
|
| |
|
Unit |
Test standard |
|
| Appearance |
Casting body with no defects |
|
|
| Barcol hardness |
≥45 |
|
GB 3854-83 |
| Heat deflection temperature |
≥80 |
℃ |
GB 1634-89 |
| Elongation at break |
≥3.0 |
% |
GB/T 2568-1995 |
| Tensile strength |
≥60 |
Mpa |
GB/T 2568-1995 |
| Modulus of elasticity for tension |
≥3000 |
Mpa |
GB/T 2568-1995 |
| Bending strength |
≥120 |
Mpa |
GB/T 2570-1995 |
| Bending modulus of elasticity |
≥3400 |
Mpa |
GB/T 2570-1995 |
| Absorbent(23±2℃) |
≤80 |
mg |
GB 1034-86 |
Packaging, storage condition:
TR-102 gel coat: Net wt 20KG metal pail. with 3 months of shelf life at 25℃. Avoid direct sunlight, and far away from heat. Keep the package tight until you use it.
TR-102 gel coat is one kind of inflammable material, should be far away from fire. Shipment should be handled according to relevant national regulations of GB190-90 for the management of dangerous goods. |
|
|
|
|
 |
|