Unsaturated polyester resin TR-196 |
| Performance index of Liquid resin: |
|
|
|
| |
|
Unit |
Test standard |
|
| Appearance |
transparent light yellow liquid |
|
|
| Acid value |
17-24 |
mgKOH/g |
GB/T 2895-82 |
| Solid |
65-70 |
% |
GB/T 7193.5-87 |
| Viscosity at 25℃ |
0.630-1.20 |
Pa.s |
GB/T 7193.5-87 |
| Typical curing performance: |
|
|
|
| |
|
Unit |
Test standard |
|
water bath at 25℃, add 2ml methyl ethyl ketone peroxide solution and 4ml cobalt isooctanoate solution into 100g resin |
| Gel time |
9.1-16.9 |
min |
see GB 7193.6-87 |
| Performance of cured resin: |
|
|
|
| |
|
Unit |
Test standard |
|
| Appearance |
Casting body with no defects |
|
|
| Barcol hardness |
≥40 |
|
GB/T 3854-83 |
| Heat deflection temperature |
≥60 |
℃ |
GB/T 1634-89 |
| Elongation at break |
≥3.0 |
% |
GB/T 2568-95 |
| Tensile strength |
≥60 |
Mpa |
GB/T 2568-95 |
| Modulus of elasticity for tension |
≥3000 |
Mpa |
GB/T 2568-95 |
| Bending strength |
≥110 |
Mpa |
GB/T 2568-95 |
| Bending modulus of elasticity |
≥3500 |
Mpa |
GB/T 2568-95 |
Packaging, storage condition:
TR-196: Net wt 220KG metal pail. with 3 months of shelf life at 25℃. Avoid direct sunlight, and far away from heat. Keep the package tight until you use it.
TR-196 is one kind of inflammable material, should be far away from fire. See manual before use. |
|
|
|
|
 |
|