Bulk pile packing
 Ceramic Raschig ring packing
| Specifications
mm |
Dia*height*thickness
mm |
Specific surface area
m²/m³ |
Void ratio
m³/m³ |
Number
n/m³ |
Pile weight
Kg/m³ |
Drying packing factor
m(-1) |
| ø 6 |
6*6*2 |
789 |
0.73 |
3110000 |
737 |
2030 |
| ø10 |
10*10*2 |
440 |
0.70 |
720000 |
700 |
1280 |
| ø15 |
15*15*2 |
330 |
0.70 |
250000 |
690 |
960 |
| ø16 |
16*16*2 |
305 |
0.73 |
192500 |
730 |
784 |
| ø25 |
25*25*2.5 |
190 |
0.78 |
49000 |
505 |
400 |
| ø40 |
40*40*5 |
126 |
0.75 |
12700 |
577 |
305 |
| ø50 |
50*50*5 |
93 |
0.81 |
6000 |
457 |
177 |
| ø80 |
80*80*9.5 |
90 |
0.68 |
1910 |
714 |
234 |
| ø100 |
100*100*10 |
70 |
0.70 |
1000 |
700 |
172 |
| ø150 |
150*150*15 |
50 |
0.68 |
295 |
790 |
142 |
cross clapboard ring
ø80-150mm cross clapboard ring can be used as support
material, Void ratio>60%,
Ceramic pall ring
packing
| Specifications
mm |
Dia*height*thickness
mm |
Specific surface area
m²/m³ |
Void ratio
m³/m³ |
Pile Number
n/m³ |
Pile weight
Kg/m³ |
Drying packing factor
m(-1) |
| ø25 |
25*25*3.0 |
220 |
0.73 |
54000 |
620 |
565 |
| ø38 |
38*38*4 |
150 |
0.75 |
13400 |
570 |
356 |
| ø50 |
50*50*5 |
120 |
0.78 |
6800 |
550 |
252 |
| ø80 |
80*80*8 |
75 |
0.80 |
1950 |
520 |
146 |
Ceramic rectangle saddle ring
packing
| Specifications
mm |
Dia*height*thickness
mm |
Specific surface area
m²/m³ |
Void ratio
m³/m³ |
Pile Number
n/m³ |
Pile weight
Kg/m³ |
Drying packing factor
m(-1) |
| ø16 |
16*12*3 |
378 |
0.71 |
269900 |
686 |
1055 |
| ø25 |
25*20*3 |
200 |
0.77 |
58230 |
544 |
434 |
| ø38 |
38*30*4 |
131 |
0.80 |
19680 |
502 |
252 |
| ø50 |
50*42*6 |
105 |
0.79 |
8243 |
470 |
213 |
| ø76 |
76*53*9 |
76 |
0.75 |
2400 |
537 |
179.4 |
Ceramic abnormal saddle ring
packing
| Specifications
mm |
Dia*height*thickness
mm |
Specific surface aream²/m³ |
Void ratio
m³/m³ |
Pile Number
n/m³ |
Pile weight
Kg/m³ |
Drying packing factor
m(-1) |
| ø25 |
25*20*3 |
190 |
0.78 |
76600 |
510 |
340 |
| ø38 |
38*30*4 |
131 |
0.84 |
24600 |
463 |
190 |
| ø50 |
50*42*6 |
88.4 |
0.81 |
7344 |
454 |
166 |
| ø76 |
76*53*9 |
58.5 |
0.77 |
1976 |
489 |
127 |
Ceramic cascade ring packing
| Specifications
mm |
Dia*height*thickness
mm |
Specific surface area
m²/m³ |
Void ratio
m³/m³ |
Pile Number
n/m³ |
Pile weight
Kg/m³ |
Drying packing factor
m(-1) |
| ø25 |
25*20*3 |
270 |
0.74 |
74000 |
624 |
172 |
| ø50 |
50*30*5 |
108.8 |
0.787 |
9091 |
516 |
223 |
| ø76 |
76*45*7 |
63.4 |
0.795 |
2517 |
426 |
126 |
Ceramic conjugation ring packing
| Specifications
mm |
Dia*height*thickness
mm |
Specific surface area
m²/m³ |
Void ratio
m³/m³ |
Pile Number
n/m³ |
Pile weight
Kg/m³ |
Drying packing factor
m(-1) |
| ø25 |
25*25*3 |
175 |
0.78 |
74000 |
490 |
350 |
| ø38 |
25*38*4 |
118 |
0.80 |
13926 |
470 |
230 |
| ø50 |
50*50*5 |
72 |
0.80 |
6317 |
470 |
140 |
Inertia
alumina ceramic ring
Properties
| Properties |
Component |
| Item |
Unit |
Value |
Component |
Assay(%) |
| SG |
g/cm3 |
2.4-3.0 |
Al2O3 |
25-75 |
| Hardness |
|
6.5 |
SiO2+Al2O3 |
≥92 |
| Water absorption |
% |
3 |
Fe2O3 |
<1 |
| Acid resistance |
% |
>99.8 |
|
|
| Alkali resistance |
% |
>84 |
SiO2,
Al2O3 is negotiation
|
|