Properties for catalyst support |
|
Type |
Composition |
Appearance |
Phase |
Bulk density
(g/cm3) |
Strength (N/P,N/cm) |
Pore Volume
(cm3/g) |
Surface area
(m2/g) |
Pore Size
A |
Water Adsorption wt% |
TC-101-1 |
Al2O3 |
φ3,φ4,φ5 extrudate |
γ |
0.5~0.6 |
100~120 |
0.5~0.6 |
180~220 |
~110 |
65~70 |
TC-101-2 |
Al2O3 |
φ3,φ4,φ5 extrudate |
γ |
0.5~0.6 |
100~120 |
0.5~0.6 |
180~220 |
~110 |
65~70 |
TC-102 |
Al2O3 |
φ3,φ4,φ5 extrudate |
γ |
0.5~0.6 |
100~120 |
≥0.6 |
280~300 |
~80 |
65~75 |
TC-103-1 |
Al2O3 |
D1.8,D3.2 trilobe |
γ |
0.5~0.6 |
90~120 |
0.4~0.5 |
140~180 |
~100 |
60~70 |
TC-103-2 |
Al2O3 |
D1.8,D3.2 trilobe |
γ |
0.5~0.6 |
90~120 |
0.4~0.5 |
140~180 |
~100 |
60~70 |
TC-104 |
Al2O3 |
D1.8,D3.2 trilobe |
γ |
0.55~0.65 |
100~150 |
0.4~0.5 |
150~200 |
~90 |
50~60 |
TC-105 |
Al2O3 |
φ3~φ5 sphere |
γ |
0.7~0.8 |
100~150 |
0.40~0.45 |
140~200 |
~100 |
≥50 |
TC-106 |
Al2O3 |
φ3~φ5 sphere |
γ |
0.6~0.7 |
80~100 |
0.45~0.5 |
140~200 |
~120 |
60~70 |
TC-107 |
Al2O3 |
φ1.2~φ3.5 sphere |
γ |
0.4~0.5 |
50~80 |
1.0~1.2 |
160~200 |
~140 |
~130 |
TC-108 |
Al2O3 |
φ1.2~φ3.5 sphere |
γ |
0.35~0.4 |
30~50 |
1.3~1.5 |
140~180 |
~220 |
~160 |
TC-109 |
Al2O3 |
φ1.2~φ3.5 sphere |
γ |
0.3~0.35 |
10~20 |
1.6~2.0 |
140~180 |
~340 |
~180 |
TC-110 |
Al2O3 |
φ1.2~φ3.5 sphere |
γ |
≤0.30 |
7~10 |
≥2.0 |
140~180 |
~500 |
~200 |
TC-111 |
Al2O3 |
multiholes |
α |
0.9~1.0 |
50~100 |
0.7~0.9 |
0.4~0.6 |
50000~400000 |
70~90 |
TC-112 |
Al2O3 |
multiholes |
α |
0.9~1.0 |
50~100 |
0.7~0.9 |
0.6~0.8 |
|
|
TC-113 |
Al2O3 |
multiholes |
α |
0.9~1.0 |
50~80 |
0.7~0.9 |
0.8~1.0 |
|
|
TC-114 |
Al2O3 |
multiholes |
α |
0.9~1.0 |
40~80 |
0.7~0.9 |
1.0~5.0 |
|
|
TC-115 |
Al2O3 |
multiholes |
α |
0.9~1.0 |
40~60 |
0.7~0.9 |
5.0~10.0 |
|
|
TC-201 |
SiO2 |
80~120mesh, microsphere |
amorphous |
0.4~0.6 |
|
0.5~0.9 |
400~600 |
~100 |
~100 |
TC-202 |
SiO2 |
80~120mesh, microballoon |
amorphous |
0.4~0.6 |
|
0.6~1.0 |
350~500 |
~100 |
~100 |
TC-203 |
SiO2 |
80~120mesh, microballoon |
amorphous |
0.3~0.4 |
|
1.5~2.0 |
300~400 |
~150 |
~150 |
TC-301 |
TiO2 |
φ3,φ5 extrudate |
anatase |
0.65~0.75 |
80~120 |
0.3~0.4 |
100~150 |
~50 |
45~55 |
TC-401 |
TiO2, Al2O3 |
φ3,φ5 extrudate |
|
0.6~0.7 |
100~120 |
0.45~0.55 |
140~180 |
~100 |
50~60 |
TC-501 |
MgO, Al2O3 |
φ3,φ5 extrudate |
spinel |
0.45~0.55 |
100~120 |
0.38~0.42 |
100~120 |
~130 |
56~60 |
TC-601 |
MgO, Al2O3, SiO2 |
monolith |
|
|
|
|
|
|
|
TC-701 |
SiO2, Al2O3 |
φ3,φ5 extrudate |
amorphous |
0.50~0.60 |
100~120 |
|
|
|
|
TC-801 |
Al2O3 |
φ3,φ5 extrudate |
γ |
0.45±0.05 |
≥80 |
|
|
|
|
|
|
|
|