It is a new-type fluorocarbon thermoplastic resin with excllent resistance to chemicals, high temperature, oxidation; high mechanical strength, good flexibility, good resistance to UV, radiation as well as excellent dielectricity, piezoelectricity and thermoelectric property.
Properties & Use
Item |
Value |
JHR-200
(mould pressing) |
JHR-500
(coating) |
JHR-400
(injection) |
Melt flow rate, g/min |
1-4 |
1-6 |
15-25 |
8-15 |
25-40 |
M.P., ℃ ≥ |
160 |
155 |
165 |
165 |
165 |
Moisture, % ≤ |
0.1 |
0.5 |
0.1 |
0.1 |
0.1 |
Relative Density, g/cm3 |
1.75-1.79 |
1.75-1.79 |
1.75-1.79 |
1.75-1.79 |
1.75-1.79 |
Tensile-strength, Mpa ≥ |
35 |
— |
40 |
40 |
35 |
Elongation at break, % ≥ |
250 |
— |
200 |
200 |
100 |
Notes
1. Should be stored in clean and dry place; avoid mixing with impurities.
2. Should not be used at above 350 centi degree to avoid toxic gas from decomposition. |