Carbon Black for Use in Rubber Industry-Specification Limits |
NO. |
Name / Project |
N115 |
N220 |
N234 |
N326 |
N330 |
N339 |
N347 |
N351 |
N375 |
N539 |
N550 |
N660 |
N774 |
1 |
I2 Absorption Numberg/kg
|
160±10 |
121±7 |
120±7 |
82±7 |
82±7 |
90±7 |
90±7 |
68±7 |
90±7 |
43±6 |
43±6 |
36±6 |
29±6 |
2 |
DBP Absorption Number 10-5m3/kg
|
113±7 |
114±7 |
125±7 |
72±7 |
102±7 |
120±7 |
124±7 |
120±7 |
114±7 |
111±7 |
121±7 |
90±7 |
72±7 |
3 |
DBP Absorption Number of
Compressed Sample 10-5m3/kg
|
89-105 |
90-106 |
94-110 |
62-74 |
80-96 |
91-107 |
91-107 |
87-103 |
88-104 |
73-89 |
77-93 |
66-82 |
57~69 |
4 |
CTAB Absorption Surface Area 103m3/kg
|
119-137 |
102-120 |
110-128 |
74-92 |
73-91 |
84-102 |
78-96 |
64-82 |
87-105 |
34-48 |
35-49 |
29-43 |
23~35 |
5 |
STSASurfaceArea103m2/kg |
124±9 |
106±9 |
112±9 |
76±9 |
75±9 |
88±9 |
83±9 |
70±9 |
91±9 |
38±9 |
39±9 |
34±9 |
29±9 |
6 |
NSA SurfaceArea103m2/kg |
127-147 |
112-126 |
112-126 |
71-85 |
71-85 |
84-98 |
78-92 |
64-78 |
86-100 |
33-45 |
34-46 |
29-41 |
25~35 |
7 |
Tint Strength % |
115-131 |
108-124 |
115-131 |
103-119 |
96-112 |
103-119 |
97-113 |
92-108 |
106-122 |
|
|
|
|
8 |
Heating Loss % ≤ |
3.0 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
2.5 |
1.5 |
1.5 |
1.5 |
1.5 |
9 |
Ash Content % ≤ |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
0.7 |
10 |
Sieve Residue % ≤ 45μm |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
0.100 |
11 |
500μm Sieve Residue % ≤ |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
0.0010 |
12 |
Impurity Materials |
None |
None |
None |
None |
None |
None |
None |
None |
None |
None |
None |
None |
None |
13 |
Pour Density kg/m3 |
345±40 |
355±40 |
320±40 |
455±40 |
380±40 |
345±40 |
335±40 |
345±40 |
345±40 |
385±40 |
360±40 |
440±40 |
490±40 |
14 |
Fines Content % ≤
|
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
15 |
Stress at 300% Elongation(by IRB7#) Mpa≥ |
-3.1±1.6 |
-2.0±1.6 |
-0.1±1.6 |
-3.6±1.6 |
-0.6±1.6 |
+0.9±1.6 |
+0.5±1.6 |
+1.1±1.6 |
+0.4±1.6 |
-1.3±1.6 |
-0.6±1.6 |
-2.3±1.6 |
-3.8±1.6 |
16 |
Stress at 300% Elongation(by IRB3#) Mpa≥ |
-3.4±1.6 |
-2.3±1.6 |
-0.4±1.6 |
-3.9±1.6 |
-0.9±1.6 |
+0.6±1.6 |
+0.2±1.6 |
+0.8±1.6 |
+0.1±1.6 |
-1.6±1.6 |
-0.9±1.6 |
-2.6±1.6 |
-4.1±1.6 |