T101 Flame Retardant |
|
For PU foam materials, mainly for chunk foam and soft polyether foam of auto, with properties of non-transmission and good compatibility.
Moisture% : 13
phosphor content % : ≤ 0.10
chlorine content %:31
acidity mgkoh/g: ≤ 0.10 |
|
CR-505 Flame Retardant |
|
As a high-molecule flame retardant, it enjoys the properties of little transmission, long flame retarding, low viscidity and compatibility, more it is easy to use and prevent burning to the heart of foam, applying to PU foam. When additive is added to a prescription, it reaches the standard of self-extinguishing.
Phosphor content %:12
moisture : ≤ 0.10
chlorine content %: 27.5
acidity mgkoh/g: ≤ 0.20 |
|
TCEP Flame Retardant |
|
It combines the phosphate ester of phosphor and chlorine, enjoying great properties of flame retarding and plasticity to the plastic and rubber products, as well as good luster, low acidity and low moisture. It is the ideal products for soft or hard PU foam, cellulose acetate, ethyl cellulose, rubber or plastic conveyor belt.
phosphor content% : 10.8
moisture% : ≤ 0.10
chlorine content% : 36.7
acidity mgkoh/g : ≤ 0.20 |
|
IPPP Flame Retardant |
|
It is applied to the plasticizing agent of natural rubber products and plastic conveyor belt of flame retarding, leather, tarpaulin, mulching film, floor material, cable, Buna-N rubber, CHR rubber, as well as the flame retardant of epoxy resin, and for the compression additive of gear oil, calendaring oil and cutting oil.moisture% : ≤ 0.10
acidity mgkoh/g : ≤ 0.20
|
|
|
|
FR-V6 Flame Retardant |
|
|
As a high-molecule flame retardant of phosphate ester, it is applied to producing polyether foam, foam of high flexibility and molding foam of flame retarding, and it enjoys great properties of flame retarding in a fairly long time and prevent scorching, especially appropriate for auto and furniture. It is an ideal substitute for equivalent exported and reduces cost as its most properties has reached or exceeded the equivalents exported.
Phosphor content % : 10.5
moisturemoisture% : ≤ 0.10
chlorine content % : 36.5
acidity mgkoh/g: ≤ 0.10 |
|
|
TCPP Flame Retardant |
|
|
It is mainly applied to soft (hard) PU foam, epoxy resin , polystyrene, acrylic acid, cellulose acetate, ethyl cellulose resin, bakelite, polyvinyl acetate, and foam gap filler, especially for thermal conduction of hard PU foam and stability of hydrolyze, as well as for the synthetic PU foam and saturation resin and bakelite with low viscosity under low temperature.
Phosphor content % : 9.5
moisture %: ≤ 0.10
chlorine content % : 32.5
acidity mgkoh/g: ≤ 0.06 |
|
|
TDCPP Flame Retardant |
|
|
It is mainly applied to soft or hard PU foam, PVC, epoxy resin, polyester fiber, rubber or plastic conveyor belt, with products of self extinguishing and the properties of light fastness, water resistance, static resistance and improving the luster of products.
phosphor content% : 7.2
moisture% : ≤ 0.10
chlorine content% : 49.4
acidity mgkoh/g : ≤ 0.20 |
|
|
*Remark :
If customer has any specific requirements on moisture and/or acidity, please show us. |
|
|