| A0510 colored OEM metal bottom color paint |
1. Characters
Used as high temperature metal bottom varnish for cars, body for trucks, part of autos and equipment Dope.
Good mechanical property, good medium resistance and good weatherability;
Tidiness flash dyes, strong third dimension and strong covering power.
2. Composition
It is made from acrylic polyol resin, amino resin, anti-flow linked resin and others to produce metal bottom varnish.
3. Construction mixture ratio
Paint:thinner=3:1or suitable construction Viscidity
4. Dope index
| Testing item |
Testing method |
Index |
| Color and appearance |
visual test |
all colors. Paint film levels up and lubricates |
| Viscidity |
GB1723-79painting four cups
°C25°C |
=40S |
| Drying time |
GB1726-79 |
140°C×30min baking |
| Solid content |
attemperation oven |
=30% |
| Rigidity |
Pencil rigidityGB1730-85 |
=H |
| Adhesive force |
single Dope ROND DE
GB1720-85 |
=Level one |
Flexibility |
flexibility testerGB1731-79 |
1 mm |
| Impact strength |
impact testerGB1732-79 |
=50 Kg·cm |
| Cupping test |
cupping testerGB/T 9753 |
=5mm |
| Petrol-resistance |
GB/T 1734(23°C×8h) |
no bubbling, no crinkle and no obviously changing colors |
| Water resistance |
GB/T 1733(23°C×240h) |
no bubbling, no crinkle and no obviously changing colors |
| Acid resistance (0.1N sulphur) |
GB/T 9274(23°C×24h) |
no bubbling, no crinkle and no obviously changing colors |
| Alkali resistance (0.1N NaOH) |
GB/T 9274(23°C×24h) |
no bubbling, no crinkle and no obviously changing colors |
| Salt-fog resistance |
GB/T 1771(240h) |
single-side corrosion=3mm |
| Artificial aging |
GB/T1865-1997(800h) |
Type I |
5. Front mating paints
Electrophoretic primer and high temperature floating coat.
This product is used in other substrate materials. Please consult our company.
6. Construction conditions
Substrate temperature well painting is about -20~50°C. Please must use spraying when the temperature is above 40°C for substrate temperature. Please must add suitable thinner to adjust Dope viscidity in order to avoid dry spraying.
7. Construction methods
Spraying:airless spraying or air spraying. Recommending adopting high pressure airless spraying. Please pay more attention to adjusting paint viscidity and air pressure when adopting air spraying.
Brushing:Suggested that it is adopted when pre-Dope and small areas Dope, but it must reach dry film thickness.
Humidity:30-75% Atomizing pressure:4-6Kg/cm2
Wind speed:0.2-0.4m/s Gun distance:200-300mm
Spraying times:two times for thin amorphous phosphating Spraying swath:200-400mm
Film thickness:20-40µm Gun speed:0.2-0.8m/s
8. Construction parameters
Mixing ratio(weight) 3:1or adjusting to suitable construction viscidity
Thinner/cleaning agent Andi series special thinner
9. Packing and storage
Packing and storage according to state regulation. Storing in dry, cool, well-ventilated conditions and avoid high temperature and keep away from fire. Packing container should be airproof. Valid storage period is one year.
10. Health and safety
Please pay more attention to warning logo on the packaging container. Using in a well-ventilated environment. Do not imbibe mist inhalation and avoid skin contact. Please immediately wash with a suitable cleaning agent, soap and water washing when splashing on the skin; please immediately go to hospital when splashing into eyes.°C |
|
|
|
|