SUQING TYPE IONIC FORM TOTAL CAPACITY meq/ml min WATER RETENTION % BULK DENSITY g/ml PARTICLE SIZE mm MAXIMUM TEMP Degree C. TOTAL REVERSIBLE SWELLING % REMARKS 201x2 Strong Base Gel Polystyrene Cl 0.75 70-78 0.65-0.70 0.4-1.25 80℃ Cl→OH≤35 Gel type I anion resin will high kinetic properties. For antibiotic extraction and organic acid adsorption. 201x4 Cl 1.30 50-56 0.65-0.72 0.4-1.25 80℃ Cl→OH≤30 With good kinetic properties and high working capacity. For deminerali-zation and silica removal. Widely used in Pharmaceatical and Food industries. 201x4FC Cl 1.20 50-56 0.63-0.72 0.6-1.25 80℃ Cl→OH≤30 For demineralization in floating bed. 201x7 Cl 1.40 42-48 0.67-0.73 0.315-1.25 80℃ Cl→OH18-22 With high capacity and good mechanical strength for deionization 201x7 OH 1.15 53-58 0.66-0.71 0.315-1.25 60℃ . 201x7FC Cl 1.40 42-48 0.67-0.73 0.45-1.25 80℃ Cl→OH18-22 For floating bed 201x7FC OH 1.10 53-58 0.66-0.71 0.45-1.25 60℃ . 201x7MB Cl 1.40 42-48 0.67-0.73 0.40-0.90 80℃ Cl→OH18-22 For ultrapure water preparation in mixed bed. Good separation property from cation resin 201x7MB OH 1.20 53-58 0.66-0.71 0.40-0.90 60℃ . 202-II Cl 1.30 45-51 0.63-0.70 0.40-1.25 80℃ Cl→OH18-22 Gel type II anion resin. With very high working capacity and regeneration efficiency. For deionization. D201 Strong Base Macroporous Polystyrene Cl 1.15 55-60 0.65-0.73 0.315-1.25 80℃ Cl→OH≤20 With very high resistance to physical breakage, osmotic shock fracture and High resistance to organic fouling. Good silica removal ability. D201 OH 0.95 58-65 0.63-0.70 0.315-1.25 60℃ . D201FC Cl 1.15 55-60 0.65-0.73 0.45-1.25 80℃ Cl→OH≤20 For high flow rate water treatment in floating bed. D201FC OH 0.95 58-65 0.63-0.70 0.45-1.25 60℃ . D201MB Cl 1.15 50-60 0.65-0.73 0.45-0.90 80℃ Cl→OH≤20 For ultrapure water preparation in mixed bed with good separation property from cation resin. D201MB OH 0.95 58-60 0.63-0.70 0.45-0.93 60℃ . D202-II Cl 1.20 50-57 0.68-0.73 0.315-1.25 80℃ Cl→OH≤15 Macroporous type II anion resin. Very high resistance to physical breakage, osmotic shock fracture and organic foaling. Very high working capacity and regeneration efficiency for deionization. D202-II OH 1.0 55-63 0.65-0.70 0.315-1.25 60℃ . D202-IIFC Cl 1.20 50-57 0.68-0.73 0.45-1.25 80℃ Cl→OH≤15 For high flow rate water treatment in floating bed. D202-IIFC OH 1.0 55-63 0.65-0.70 0.45-1.25 60℃ . D208 Cl 0.5-0.6 78-85 0.63-0.70 0.6-1.6 80℃ Cl→OH≤15 Macroporous type I anion resin with very good kinetic property. Suited for Heparin sodium separation and purification. High Heparin sodium selectivity. D301-III Weak Base Macroporous Polystyrene Free base 1.40 50-58 0.65-0.72 0.315-1.25 100℃ Cl→OH≤20 Macroporous weak base anion resin. With superior mechanical and osmotic strength.. Good kinetic property and very high working capacity for demineralization. Easy to be generated. D301-IIIFC 1.40 50-58 0.65-0.72 0.45-1.25 100℃ . Used in floating bed. D301-G 1.50 48-55 0.65-0.72 0.4-1.25 100℃ Cl→OH≤25 Superior mechanical and osmotic strength. High resistance to organic fouling and high capacity. For demineralization and decolorization of sacchrose, fructose, glucose and other organic solutions. D311 Weak Base Macroporous Polyacrylic 2.0 53-58 0.70-0.75 0.315-1.25 100℃ Cl→OH≤15 Excellent mechanical and osmotic strength and very high capacity. For demineralization and decolorization of organic solutions. D218 Strong Base Macroporous Polyacrylic   1.35 55-65 0.65-0.75 0.4-1.25 38℃ Cl→OH≤7 Preparing pure water, decolor for syrup  D318 Weak Base Macroporous Polyacrylic Free base 2.2 55-65 0.70-0.80 0.4-1.25 60℃ Cl→OH≤18 Abstraction and decolor for citric acid vitamin C

Thinker Information & Techology Ltd,co.of Wuxi City
Copyright©1999 - 2000