SUQING |
TYPE |
IONIC
FORM |
TOTAL
CAPACITY
meq/ml
min |
WATER
RETENTION
% |
BULK
DENSITY
g/ml |
SCREEN
SIZE
mm |
MAXIMUM
TEMP
Degree
C. |
TOTAL
REVERSIBLE
SWELLING
% |
REMARKS |
| 1.Tribed
Specially Resins |
|
D001-TR |
Strong
Acid
Macroporous
Polystyrene |
Na+ |
1.7 |
45-50 |
0.75-0.80 |
0.70-1.25 |
120 |
Na-H 5-8 |
Defintive organization
for deionization in high flow rate. Flow rate up to 80m/h. spcific
Gravity of STR inert resin is 1.14-1.16. The presence of inert resin
makes the separation of cation and anion resin very easy. |
|
D201TR |
Strong
Base
Macroporous
Polystyrene |
Cl- |
1.2 |
55-60 |
0.67-0.72 |
0.45-0.90 |
60 |
Cl-OH18-20 |
|
S-TR |
Inert
Polymeth-
acrylate |
/ |
/ |
< 6 |
0.67-0.72 |
0.70-0.90 |
120 |
/ |
| 2.Condensate
Polishing Resins |
|
D003NJ |
Strong
Acid
Macroporous
Polystyrene |
Na |
1.90 |
42-48 |
0.8-0.85 |
0.65-0.85 |
120 |
Na-H 5-8 |
Definitive organization
for condensate polishing. Excellent resistance to physical breakage.
Osmatic shock fracture and oxidation used in Low pressure or Medium
pressure Boiler Conden-sate polishing. The flow rate can be up to
120 m/h. |
|
D203NJ |
Strong
Base
Macroporous
Polystyrene |
Cl |
1.40 |
42-48 |
0.66-0.72 |
0.45-0.65 |
80¡æ |
Cl-OH ¡Ü15 |
| 3.Caralyst
Resins |
|
002CR |
Strong
Acid
Gel
Polystyrene |
H |
5.0
(mmol/g) |
55-65 |
0.72-0.78 |
0.5-1.0 |
100 |
/ |
Super-gel
strong acid resin.With high activity, high selectivity and high mechanical
strength. Used mainly for bisphenol A preparation. Dry resin is also
available (water retention 5-10%) |
|
D002 |
Strong
Acid
Macroporous
Polystyrene |
H |
4.8
(mmol/g) |
48-55 |
0.75-0.80 |
0.4-1.25 |
100 |
/ |
Used mainly
for MTBE preparation. High catelytic activity, high selectivity and
high mechanical strength. Surface area 35-45 m2/g, pore
volume 0.3-0.4ml/g, average pore diameter 20-50nm. Dry resin is also
available (water retention 3-5%). |
| 4.Chelating
Resins |
|
D401 |
Macroporous
Polystyrene |
Na |
0.6(CU2+) |
52-58 |
0.72-0.78 |
0.4-1.25 |
100 |
H-Na ¡Ü40 |
Macroporous
iminodiacetate resin. Highly selective for multi-valence metal ions.
For separation of heavy and scarce metals. |
|
D402 |
. |
Na |
0.5(Ca2+) |
52-58 |
0.72-0.78 |
0.4-1.25 |
100 |
H-Na ¡Ü40 |
Macroporous
aminophos-phonic resin. High capacity for
Ca2+ and Mg2+. For removal of hardness from
brine. |
|
D403 |
. |
Free base |
1.0 |
48-53 |
0.72-0.78 |
0.4-1.25 |
100 |
OH-Cl ¡Ü40 |
Chelating
resin specific for boron adsorption. |
|
D405 |
. |
H |
1.2 |
45-50 |
0.72-0.78 |
0.4-1.25 |
70 |
/ |
Chelating
resin specific for mercury removal. |
|
D407 |
|
cl |
1.2
|
50-60
|
0.65-0.75
|
0.4-1.25
|
100
|
/
|
chelating
resin specific for nitrate radical removal |
|
SQ407 |
|
cl |
1.2
|
53-63 |
0.65-0.75 |
0.25-0.84 |
80 |
|
chelating resin specific for arsenic removal |
| 5.Adsorbent
Resins |
|
SUQING |
TYPE |
WATER RETENION % |
BULK DENSITY g/ml |
SPECIFIC GRAVITY g/ml |
PARTICLE
SIZE
mm |
SURFACE AREA
m2/g |
AVERAGE PORE DIAMETER
(mm) |
PORE VOLUME ml/g |
REMARKS |
|
DA201-A |
Polystyrene
Macroporous |
45-50 |
0.65-0.70 |
1.03-1.07 |
0.4-1.25
|
400-450 |
10-11 |
1.1-1.2 |
Macroporous
non-polar adsorbent resin. Used mainly for biochemicals adsorption. |
|
DA201-B |
50-55 |
0.65-0.70 |
1.03-1.07 |
500-600 |
8-9 |
1.1-1.2 |
Macroporous
non-polar adsorbent resin. Used mainly for stevia extraction, biochemicals
adsorption. |
|
DA201-C |
50-55 |
0.72-0.78 |
1.07-1.13 |
900-1100 |
35-45 |
1.0-1.1 |
Macronet
non-polar adsorbent resin. Used mainly for adsorption of phenol and
other organic substances, decolorization, etc. |
| DA201-D |
|
30-40
|
0.65-0.75
|
1.02-1.07
|
0.315-1.25 |
600-800 |
5-7 |
1.5-2.5
|
mainly
used for decolor in fruit juice |