SUQING |
TYPE |
IONIC
FORM |
TOTAL
CAPACITY
meq/ml
min |
WATER
RETENTION
% |
BULK
DENSITY
g/ml |
PARTICLE
SIZE
mm |
MAXIMUM
TEMP
Degree
C. |
TOTAL
REVERSIBLE
SWELLING
% |
REMARKS |
|
001x4 |
Strong
Acid
Gel Polystyrene |
Na |
1.40 |
52-58 |
0.75-0.80 |
0.4-1.25 |
120 |
Na To H 10-15 |
With excellent
kinetic property, mainly used in softening, demineralisation
and antibiotic purfication. |
|
001x4 |
H |
1.25 |
58-65 |
0.72-0.78 |
0.4-1.25 |
100 |
. |
|
001x7 |
Na |
1.95 |
45-50 |
0.78-0.85 |
0.315-1.25 |
120 |
8-10 |
Gel type standard.
Suitable for softening
demineralisation. |
|
001x7 |
H |
1.80 |
51-56 |
0.73-0.80 |
0.315-1.25 |
100 |
. |
|
001x7FC |
Na |
1.95 |
45-50 |
0.78-0.85 |
0.45-1.25 |
120 |
8-10 |
For softening
and demineralisation, mainly used in floating bed. |
|
001x7FC |
H |
1.80 |
51-56 |
0.73-0.80 |
0.45-1.25 |
100 |
. |
|
001x7MB |
Na |
1.80 |
45-50 |
0.77-0.83 |
0.71-1.25 |
120 |
8-10 |
For ultrapure
water preparation, Give good separation from anion resin in mixed
bed. |
|
001x7MB |
H |
1.70 |
51-56 |
0.73-0.80 |
0.71-1.25 |
100 |
. |
001x8 |
Na |
2.0 |
43-48 |
0.78-0.88 |
0.315-1.25 |
120 |
8-10 |
mainly used
for softening hard water and preparing pure and high purity water |
001x8FC |
Na |
2.0 |
43-48 |
0.78-0.88 |
0.45-1.25 |
120 |
5-8 |
001x8MB |
Na |
2.0 |
43-48 |
0.78-0.88 |
0.71-1.25 |
120 |
5-8 |
|
001x10 |
Na |
2.2 |
37-42 |
0.80-0.85 |
0.45-1.25 |
120 |
5-8 |
With high resistance
to physical breakage, osmotic shock fracture and oxidation. For softening
and deionization, particularly suited for use in mixed bed. Available
in black color for easy visual separation in mixed bed. |
|
001x10 |
H |
2.1 |
43-50 |
0.78-0.83 |
0.15-1.25 |
100 |
. |
|
D001 |
Strong
Acid Macroporous Polystyrene |
Na |
1.9 |
45-50 |
0.78-0.85 |
0.315-1.25 |
120 |
5-8 |
With very high
resistance to physical breakage, osmotic shock fracture and high resistance
to organic fouling. |
|
D001 |
H |
1.8 |
50-55 |
0.75-0.80 |
0.315-1.25 |
100 |
. |
|
D001FC |
Na |
1.9 |
45-50 |
0.78-0.85 |
0.45-1.25 |
120 |
5-8 |
Basic properties
same as D001, mainly used in floating bed. For high rate softening
and deionization. |
|
D001FC |
H |
1.8 |
50-55 |
0.75-0.80 |
0.45-1.25 |
100 |
. |
|
D001MB |
Na |
1.8 |
45-50 |
0.75-0.83 |
0.63-1.25 |
120 |
5-8 |
Basic properties
same as D001, mainly used in mixed bed. For high flow rate ultrapore
water preparation |
|
D001MB |
H |
1.7 |
50-55 |
0.72-0.79 |
0.63-1.25 |
100 |
. |
|
D113-III |
Weak Acid
Macroporous
Polystyrene |
H |
4.5 |
45-50 |
0.74-0.80 |
0.325-1.25 |
100 |
H to Na
¡Ü 65 |
With
excellent resistance to physical breakage, osmotic shock fracture
and high resistance to organic fouling. With High total capacity and
working capacity. For softening and dealkalization. |
|
D113-IIIFC |
H |
4.4 |
45-50 |
0.72-0.78 |
0.45-1.25 |
100 |
Basic
properties same as D113-III. Used for softening and dealkalization
in floating bed. |
|
D113-IIISC |
H |
4.5 |
45-50 |
0.74-0.80 |
0.355-0.63 |
100 |
Basic
properties same as D113-III. Used for softening and dealkalization
with 001X7 in bilayer bed. |