Product Specifications
National Standard of 4-3 Loose Type Polyvinyl Chloride(GB8761-86)
Table 1:
NO. |
Item/Grade/Type |
PVC-SG1 |
PVC-SG2 |
PVC-SG3 |
PVC-SG4 |
First Grade A
|
First Grade |
Second Grade |
First Grade |
Second Grade |
First Grade |
Second Grade |
A |
B
|
A |
B
|
A |
B
|
1 |
Viscosity Number
mL/g |
154-144 |
143-136 |
135-127 |
126-118 |
2 |
Apparent Densityg/M1 |
0.42 |
0.42 |
0.42 |
0.40 |
0.42 |
0.42 |
0.40 |
0.42 |
0.42 |
0.40 |
3 |
Plasticizer Absorption of 100g Resin, g
≥ |
25 |
25 |
25 |
16 |
25 |
25 |
16 |
22 |
22 |
16 |
4 |
Volatile matter(include water) Content%≤ |
0.40 |
0.40 |
0.40 |
0.50 |
0.40 |
0.40 |
0.50 |
0.40 |
0.40 |
0.50 |
5 |
Sieving Rate% |
60 meshes 0.25mm sieve pore ≥ |
98.0 |
98.0 |
98.0 |
92.0 |
98.0 |
98.0 |
92.0 |
98.0 |
98.0 |
92.0 |
250 meshes 0.063mm sieve pore≤ |
10.0 |
10.0 |
10.0 |
20.0 |
10.0 |
10.0 |
20.0 |
10.0 |
10.0 |
20.0 |
6 |
Total number of black-yellow spot per 100g resin adnd number of black spot≤ |
Total number |
30 |
30 |
30 |
130 |
30 |
30 |
130 |
30 |
30 |
130 |
Number of black spot |
10 |
10 |
10 |
30 |
10 |
10 |
30 |
10 |
10 |
30 |
7 |
Whiteness
% ≥ |
90 |
90 |
90 |
85 |
90 |
90 |
85 |
90 |
90 |
85 |
8 |
Number of fish eye, per 1000
cm2 ≤ |
10 |
10 |
|
|
10 |
|
|
10 |
|
|
9 |
Conductivity of 10% resin water extractI/(O, cm)≤ |
5×10-6 |
5×0-5 |
|
|
5×0-5 |
|
|
|
|
|
10 |
Residual vinyl chloride gas content ppm
≤ |
10 |
10 |
10 |
|
10 |
10 |
|
10 |
10 |
|
11 |
Thermal stability of resin |
to be determined |
|
|
|
|
|
|
|
|
|
National Standard of 4-3 Loose Type Polyvinyl Chloride(GB8761-86)
Table 2:
NO. |
Item/Grade/Type |
PVC-SG5 |
PVC-SG6 |
PVC-SG7 |
First Grade |
Second Grade |
First Grade |
Second Grade |
First Grade |
Second Grade |
A |
B
|
A |
B
|
A |
B
|
1 |
Viscosity Number
mL/g |
117-107 |
105-96 |
95-85 |
2 |
Apparent Densityg/M1 |
0.45 |
0.45 |
0.45 |
0.45 |
0.45 |
0.40 |
0.15 |
0.45 |
0.40 |
3 |
Plasticizer Absorption of 100g Resin, g
≥ |
19 |
19 |
13 |
16 |
16 |
13 |
14 |
14 |
13 |
4 |
Volatile matter(include water) Content%≤ |
0.40 |
0.40 |
0.50 |
0.40 |
0.40 |
0.50 |
0.40 |
0.40 |
0.50 |
5 |
Sieving Rate % |
60 meshes 0.25mm sieve pore ≥ |
98.0 |
98.0 |
92.0 |
98.0 |
98.0 |
92.0 |
98.0 |
98.0 |
92.0 |
250 meshes 0.063mm sieve pore≤ |
10.0 |
10.0 |
20.0 |
10.0 |
10.0 |
20.0 |
10.0 |
10.0 |
20.0 |
6 |
Total number of black-yellow spot per 100g resin adnd number of black spot≤ |
Total number |
30 |
30 |
130 |
30 |
-30 |
130 |
30 |
30 |
130 |
|
10 |
10 |
30 |
10 |
10 |
30 |
10 |
10 |
30 |
7 |
Whiteness
% ≥ |
90 |
90 |
85 |
90 |
90 |
85 |
90 |
90 |
85 |
8 |
Number of fish eye, per 1000cm2
≤ |
10 |
|
|
10 |
|
|
10 |
|
|
9 |
Conductivity of 10% resin water extract I/(O
Number of black spot
, cm)≤ |
|
|
|
|
|
|
|
|
|
10 |
Residual vinyl chloride gas content ppm
≤ |
10 |
10 |
|
10 |
10 |
|
10 |
10 |
|
11 |
Thermal stability of resin |
|
|
|
|
|
|
|
|
|
|
|